| Abstract |
| This paper surveys emission characteristics of Far-infrared of the fabrics fabricated with germanium imbedded sheath-core conjugate composite filaments. For this purpose, master batch chip was prepared with PET semi-dull chip and nano sized germanium particles and sheath-core type conjugate composite filament was spun using this master batch chip and polyester semi dull. The emission power and emissivity of the germanium imbedded fabrics were measured and investigated using FT-IR spectrophotometer by KICM- FIR 1005 measurement method. In addition, the fabric mechanical properties were measured and discussed with the effects of the optimum texturing process conditions and fabric structural design conditions. The sheath/core type PET composite germanium imbedded filaments were manufactured by the optimum spinning condition, its tenacity and breaking strain showed the same level as the regular PET filament. The tenacity and breaking strain of the DTY showed good physical properties and no problem in the weaving process. Then, wet and dry shrinkages showed higher values than those of regular PET filament. The emission power of the germanium imbedded fabric was 3.53×102W/m2 at the 5-20㎛wave length range, and emissivity was 0.874. The fabric hand of germanium imbedded fabrics was inhanced by the optimum texturing process and fabric structural design with improved mechanical properties such as fabric bending and compressional properties. |
|
|
| Key Words |
| 게르마늄, 원적외선, 방사강도, 방사율, 마스터배치, 직물밀도 계수, Germanium, Far-infrared, Emission power, Emissivity, Master-batch, Weave density coefficient |
|
|
 |
|